Semiconductor thin film and liquid crystal display apparatus using the same, and method of fabricating the same

ABSTRACT

A crystalline semiconductor having an even surface and a large crystal grain size is formed on an economical glass substrate using a laser crystallizing technology. A series of processes, including forming an insulation film on a glass substrate; forming a semiconductor film in the first layer; crystallizing the semiconductor film in the first layer by irradiating laser light stepwise from weak energy laser light to strong energy laser light; forming a semiconductor film in a second layer having a film thickness thinner than that of the semiconductor film in the first layer; performing laser crystallization of the semiconductor thin film in the second layer by irradiating laser light stepwise from weak energy laser light to strong energy laser light, are continuously performed without exposing the workpiece to the atmosphere.

BACKGROUND OF THE INVENTION

[0001] The present invention relates to a semiconductor thin film that is fabricated by a laser crystallizing method, as well as a thin film transistor and semiconductor devices, such as a liquid crystal display apparatus, an active matrix type liquid crystal apparatus, a solar cell and the like, which use the semiconductor thin film, and a method of fabricating the semiconductor thin film, the thin film transistor and the semiconductor devices.

[0002] The laser crystallizing technology is most widely viewed as a means to fabricate a crystalline semiconductor at a low cost, which crystalline semiconductor is of the type which is applied to a high performance thin film transistor, a high value-added liquid crystal display apparatus and a solar cell. Because the crystallization of a semiconductor thin film locally heats only the vicinity of the semiconductor surface by laser irradiation, a low-cost glass substrate and a low-cost organic resin substrate can be used for the supporting substrate, and, accordingly, the laser crystallizing technology contributes to a reduced cost. Since the laser-irradiated semiconductor is first liquefied and then solidified so as to be crystallized, a high-quality crystalline semiconductor having less defects can be obtained. One way to improve the film quality of the crystalline semiconductor is to increase the crystal grain size. By increasing the crystal grain size, the volumetric ratio of the crystal grain boundary, including defects, to the whole semiconductor film is decreased, and, consequently, the mobility of electrons and holes is improved. Further, a decrease itself in number of the defects improves the quality of the crystalline semiconductor. In regard to a way to increase the crystal grain size, (1) Dig. Of Tech. Papers, 1997, Int. Workshop Active Matrix Liquid Crystal Display (Business Center of Academic Societies, Tokyo 1997), p59, proposes a method in which, after crystallizing an amorphous silicon by laser irradiation, an amorphous silicon film is formed on the fabricated polycrystalline silicon, and then the amorphous silicon is crystallized by laser irradiation.

[0003] On the other hand, a problem of the crystalline semiconductor, for example, the polycrystalline silicon fabricated by a laser crystallizing method, concerns the formation of an uneven surface due to many projections which are produced when a high-quality polycrystalline silicon having large crystal grain size is fabricated. The height of the projections is nearly equal to the film thickness of the semiconductor before irradiating the laser light. A mechanism for producing such projection is considered in the Applied Physics Letters, Vol.68, No.15, 1996, p2138, which indicates that the projections are formed by volumetric expansion caused by the phase transition from the melted silicon to the solid silicon at a boundary where surfaces of crystal growth in a direction lateral to the substrate surface collide with each other. The crystal growth in the lateral direction generally occurs when a crystal having a crystal grain size larger than the thickness of the semiconductor thin film is formed. When a semiconductor thin film having large unevenness is used to form the active layer of a coplanar type thin film transistor, the concentration of an electric field occurs at the projections so as to cause dielectric breakdown in the gate insulation film serving as the upper layer, of the active layer or to cause reduction of the reliability of the gate insulation film such as by production of defects due to hot carriers. In order to protect against these problems, the thickness of the gate insulation film needs to be formed so as to be thicker than 100 nm, and, consequently, it becomes difficult to drive the thin film transistor with low power consumption. Further, since the crystallinity of the projection is very low and the projection is located in a channel area when the semiconductor having many projections is used for a coplanar type or a normal stagger type thin film transistor, the ON current is reduced. In regard to techniques for suppressing the occurrence of the projections when the semiconductor thin film is crystallized with laser light, the following techniques have been reported.

[0004] (2) A method of irradiating laser light in stages with a pitch of 10 mJ/cm2 is described in IEEE TRANSACTIONS ON ELECTRON DEVICES, Vol.42, No.2, 1995, p251.

[0005] (3) A method of irradiating laser light after poly-crystallizing amorphous silicon using a solid phase growth method is described in Dig. of Tech. Papers 1997, Int. Workshop Active Matrix Liquid Crystal Displays (Business Center of Academic Societies, Tokyo 1997), p167.

[0006] (4) A method of changing the shape of a laser beam so as to have a wide lower slopes is described in Shin-etsu Chemical Technical Report EID98-19 (1998-06), p67.

[0007] The above-described conventional technology (1) which proposes to increase the crystal grain size of the crystalline semiconductor has a problem in that the crystal grain size can be certainly increased, but projections having a height nearly equal to the film thickness of the semiconductor are produced, and, accordingly, a large unevenness is produced. Further, there is another problem in that, because the amorphous silicon before laser irradiation is exposed to the atmosphere in order to perform dehydrogenation and, thereby, a natural oxide film is formed on the surface, oxygen enters into the silicon film when it is crystallized by laser light to reduce the quality of the film.

[0008] On the other hand, the conventional technology (2) for suppressing production of the projections has a problem in that, since laser light is irradiated in stages with a small pitch of 10 mJ/cm² and the fine crystalline silicon that is first formed is difficult to melt, what can be fabricated is only polycrystalline silicon having a crystal grain size of nearly 60 nm, and, accordingly, polycrystalline silicon having a large crystal grain size above 500 nm can not be fabricated. The conventional technology (3) for suppressing production of the projections has a problem in that, because the solid phase growth method is used and, consequently, the silicon is heated at 1000° C., an economical glass substrate can not be used, and, accordingly, the crystalline semiconductor can not be fabricated with a low cost. The conventional technology (4) for suppressing production of the projections has a problem in that, since the crystal grain size becomes small as the projection is made small, the small roughness and the large crystal grain size are not compatible with each other.

SUMMARY OF THE INVENTION

[0009] An object of the present invention is to increase the crystal grain size and suppress the formation of projections on the semiconductor surface so as to be compatible with each other.

[0010] Another object of the present invention is to provide a flat crystalline semiconductor of high performance, which is low in cost and which has a film thickness above 5 nm, an average crystal grain size above 500 nm and an average surface roughness below 5 nm.

[0011] In order to solve the above-mentioned problems, a 1st aspect in accordance with the present invention is directed to a semiconductor thin film which is characterized by the fact that the semiconductor thin film is formed on a glass substrate by a laser crystallizing method, and it has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm.

[0012] A 2nd aspect in accordance with the present invention is directed to a semiconductor thin film which is characterized by the fact that the semiconductor thin film is formed on a glass substrate by a laser crystallizing method, and it has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when the surface area of an arbitrary crystal grain is expressed by Sn and the circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2).

[0013] A 3rd aspect in accordance with the present invention is directed to a semiconductor thin film which is characterized by the fact that the semiconductor thin film is formed on a glass substrate by a laser crystallizing method, and it has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when the surface area of an arbitrary crystal grain is expressed by Sn and the circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2), and further, when crystal structures on an arbitrary cross section of the crystalline semiconductor thin film are observed, at least more than 70% of the crystal grains continuously extend from an interface between the semiconductor layer and a base layer to the semiconductor surface without discontinuity at some midpoint.

[0014] A 4th aspect in accordance with the present invention is directed to a semiconductor thin film which is characterized by the fact that the semiconductor thin film is formed on a glass substrate by a laser crystallizing method, and it has a film thickness thicker than 40 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm.

[0015] A 5th aspect in accordance with the present invention is directed to a semiconductor thin film which is characterized by the fact that the semiconductor thin film is formed on a glass substrate by a laser crystallizing method, and it has a film thickness thicker than 40 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when the surface area of an arbitrary crystal grain is expressed by Sn and the circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π))^(1/2).

[0016] In addition to the characteristics of the semiconductor thin film of the 1st, the 2nd, the 3rd, the 4th or the 5th aspects of the invention, a 6th aspect in accordance with the present invention is directed to a semiconductor thin film which is characterized by the fact that the orientation of the semiconductor thin film is mainly in the (1. 1. 1) plane.

[0017] In addition to the characteristics of the semiconductor thin film of the 1st, the 2nd, the 3rd, the 4th, the 5th or the 6th aspects of the invention, a 7th aspect in accordance with the present invention is directed to a semiconductor thin film which is characterized by the fact that the semiconductor is made of silicon.

[0018] In addition to the characteristics of the semiconductor thin film of the 1st, the 2nd, the 3rd, the 4th, the 5th, the 6th or the 7th aspects of the invention, an 8th aspect in accordance with the present invention is directed to a semiconductor thin film which is characterized by the fact that at least a part of the crystal grain boundaries are positioned, and orientation of that part of the crystal grains is mainly, in the (1. 0. 0) plane or (1. 1. 0) plane.

[0019] In addition to the characteristics of the semiconductor thin film of the 1st, the 2nd, the 3rd, the 4th, the 5th, the 6th, the 7th or 8th aspects of the invention, a 9th aspect in accordance with the present invention is directed to a semiconductor thin film which is characterized by the fact that the glass substrate is made of a no-alkali glass, which has a softening point lower than 700° C.

[0020] A 10th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor thin film which is characterized by the fact that the method comprises the steps of forming an insulation film on a glass substrate; forming a semiconductor thin film on the insulation film; and continuously following the semiconductor thin film forming with crystallizing of the formed semiconductor thin film by irradiating laser light without exposing it to the atmosphere, wherein the steps of forming the semiconductor thin film and crystallizing the semiconductor thin film by irradiating it with laser light are repeated at least two times, and the irradiating of the laser light in each of the steps is such that energy of the laser light is increased in steps from scanning of a weak energy laser light to scanning of a strong energy laser light.

[0021] An 11th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor thin film which is characterized by the fact that the method comprises the steps of forming an insulation film on a glass substrate; forming a semiconductor thin film on the insulation film; and continuously following the semiconductor thin film forming with crystallizing of the formed semiconductor thin film by irradiating laser light without exposing it to the atmosphere, wherein the step of forming the semiconductor thin film and crystallizing the semiconductor thin film by irradiating it with laser light are repeated at least two times, and the thickness of the film in an upper layer at the time of semiconductor film forming is thinner than thickness of the film in a lower layer.

[0022] In addition to the characteristic of the fabricating method of the 10th or the 11th aspects of the invention, a 12th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor thin film which is characterized by the fact that the film thickness of the semiconductor thin film formed in the first layer is within a range of 30 nm to 70 nm, and the film thickness of the semiconductor thin film formed in the second layer is within a range of 25 nm to 40 nm.

[0023] In addition to the characteristics of the fabricating method of the 10th, the 11th or the 12th aspects of the invention, a 13th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor thin film which is characterized by the fact that the formed semiconductor thin film is silicon having a concentration of combined hydrogen in the film of less than 10%.

[0024] In addition to the characteristics of the fabricating method of the 10th, the 11th, the 12th or the 13th aspects of the invention, a 14th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor thin film which is characterized by the fact that the temperature of the substrate during the laser crystallization is within a range of 200° C. to 500° C.

[0025] In addition to the characteristics of the fabricating method of the 10th, the 11th, the 12th, the 13th or the 14th aspects of the invention, a 15th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor thin film which is characterized by the fact that the glass substrate used is a no-alkali glass and has a softening point lower than 700° C.

[0026] A 16th aspect in accordance with the present invention is directed to a semiconductor apparatus containing a thin film transistor which is characterized by the fact that the thin film transistor is formed on a glass substrate, and a semiconductor thin film formed in an active layer of the thin film transistor through a laser crystallizing method has a thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm.

[0027] A 17th aspect in accordance with the present invention is directed to a semiconductor apparatus containing a thin film transistor which is characterized by the fact that the thin film transistor is formed on a glass substrate, and a semiconductor thin film formed in an active layer of the thin film transistor through a laser crystallizing method has a thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when the surface area of an arbitrary crystal grain is expressed by Sn and the circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2).

[0028] An 18th aspect in accordance with the present invention is directed to a semiconductor apparatus containing a thin film transistor which is characterized by the fact that the thin film transistor is formed on a glass substrate, and a semiconductor thin film formed in an active layer of the thin film transistor through a laser crystallizing method has a thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when the surface area of an arbitrary crystal grain is expressed by Sn and the circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn (Sn/π)^(1/2), and further, when crystal structures on an arbitrary cross section of the crystalline semiconductor thin film are observed, at least more than 70% of the crystal grains continuously extend from an interface between the semiconductor layer and a base layer to the semiconductor surface without a discontinuity at some midpoint.

[0029] A 19th aspect in accordance with the present invention is directed to a semiconductor apparatus containing a thin film transistor which is characterized by the fact that the thin film transistor is formed on a glass substrate, and the semiconductor thin film of the 4th, the 5th, the 6th, the 7th, the 8th or the 9th aspects of invention is used in an active layer of the thin film transistor.

[0030] A 20th aspect in accordance with the present invention is directed to a semiconductor apparatus containing a coplanar type or a normal stagger type thin film transistor which is characterized by the fact that the thin film transistor is formed on a glass substrate, and the semiconductor thin film of the 1st, the 2nd, the 3rd, the 4th, the 5th, the 6th, the 7th, the 8th or the 9th aspects of the invention is used in an active layer of the thin film transistor, and the film thickness of a gate insulation film of the thin film transistor is thinner than 80 nm or the ratio of the film thickness of the gate insulation film to a film thickness of the active layer is smaller than 8/6.

[0031] A 21st aspect in accordance with the present invention is directed to a semiconductor apparatus containing a coplanar type or a normal stagger type thin film transistor which is characterized by the fact that the thin film transistor is formed on a glass substrate, and the semiconductor thin film of the 1st, the 2nd, the 3rd, the 4th, the 5th, the 6th, the 7th, the 8th or the 9th aspects of the invention is used in an active layer of the thin film transistor, and the film thickness of a gate insulation film of the thin film transistor is thinner than the film thickness of the active layer.

[0032] In addition to the characteristics of the semiconductor apparatus of the 16th, the 17th, the 18th, the 19th the 20th or the 21st aspects of the invention, a 22nd aspect in accordance with the present invention is directed to a semiconductor apparatus containing a thin film transistor which is characterized by the fact that the glass substrate is made of a no-alkali glass which has a softening point lower than 700° C.

[0033] A 23rd aspect in accordance with the present invention is directed to a semiconductor apparatus containing a solar cell which is characterized by the fact that a semiconductor thin film formed at least in a first layer in semiconductor layers of the solar cell through a laser crystallizing method has a thickness thicker than 40 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm.

[0034] A 24th aspect in accordance with the present invention is directed to a semiconductor apparatus containing a solar cell which is characterized by the fact that a semiconductor thin film formed at least in a first layer in semiconductor layers of the solar cell through a laser crystallizing method has a thickness thicker than 40 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when the surface area of an arbitrary crystal grain is expressed by Sn and the circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2).

[0035] A 25th aspect in accordance with the present invention is directed to a semiconductor apparatus containing a solar cell which is characterized by the fact that a semiconductor thin film formed at least in a first layer in semiconductor layers of the solar cell through a laser crystallizing method has a thickness thicker than 40 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when the surface area of an arbitrary crystal grain is expressed by Sn and the circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2), and further, when crystal structures on an arbitrary cross section of the crystalline semiconductor thin film are observed, at least more than 70% of the crystal grains continuously extend from an interface between the semiconductor layer and a base layer to the semiconductor surface without a discontinuity at some midpoint.

[0036] A 26th aspect in accordance with the present invention is directed to a semiconductor apparatus containing a solar cell which is characterized by the fact that the semiconductor thin film of the 1st, the 2nd, the 3rd, the 6th, the 7th, the 8th or the 9th aspects of the invention is used at least in a first layer in semiconductor layers of the solar cell.

[0037] A 27th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor apparatus containing a thin film transistor which is characterized by the fact that the method of fabricating the semiconductor thin film of the 10th, the 11th, the 12th, the 13th, the 14th or the 15th aspects of the invention is applied to fabrication of an active layer of the thin film transistor.

[0038] A 28th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor apparatus containing a solar cell which is characterized by the fact that the method of fabricating the semiconductor thin film of the 10th, the 11th, the 12th, the 13th, the 14th or the 15th aspects of the invention is applied to fabrication of at least a first layer in semiconductor layers of the solar cell.

[0039] A 29th aspect in accordance with the present invention is directed to a semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel or a peripheral circuit, wherein the semiconductor apparatus is characterized by the fact that a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the thin film transistor of the 16th, the 17th, the 18th, the 19th, the 20th, the 21st or the 22nd aspects of the invention is used for the drive element in the pixel or the peripheral circuit of the active matrix type liquid crystal display apparatus.

[0040] A 30th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel or a peripheral circuit, wherein the method is characterized by the fact that a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the method of fabricating a thin film transistor of the 27th aspects of the invention is applied to fabrication of the thin film transistor of the active matrix type liquid crystal display apparatus.

[0041] A 31st aspect in accordance with the present invention is directed to a semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel and one of electrodes of a signal storage capacitor in the pixel is formed of a semiconductor thin film in the same layer as an active layer of the thin film transistor, wherein the semiconductor apparatus is characterized by the fact that a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the semiconductor thin film forming the one of the electrodes of a signal storage capacitor in the pixel of the active matrix type liquid crystal display apparatus has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm.

[0042] A 32nd aspect in accordance with the present invention is directed to a semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel and one of the electrodes of a signal storage capacitor in the pixel is formed of a semiconductor thin film in the same layer as an active layer of the thin film transistor, wherein the semiconductor apparatus is characterized by the fact that a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the semiconductor thin film forming the one of the electrodes of the signal storage capacitor in the pixel of the active matrix type liquid crystal display apparatus has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when the surface area of an arbitrary crystal grain is expressed by Sn and the circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2).

[0043] A 33rd aspect in accordance with the present invention is directed to a semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel and one of the electrodes of a signal storage capacitor in the pixel is formed of a semiconductor thin film in the same layer as an active layer of the thin film transistor, wherein the semiconductor apparatus is characterized by the fact that a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the semiconductor thin film forming the one of the electrodes of the signal storage capacitor in the pixel of the active matrix type liquid crystal display apparatus has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when the surface area of an arbitrary crystal grain is expressed by Sn and the circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2), and further when crystal structures on an arbitrary cross section of the crystalline semiconductor thin film are observed, at least more than 70% of the crystal grains continuously extend from an interface between the semiconductor layer and a base layer to the semiconductor surface without a discontinuity at some midpoint.

[0044] A 34th aspect in accordance with the present invention is directed to a semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel and one of the electrodes of a signal storage capacitor in the pixel is formed of a semiconductor thin film in the same layer as an active layer of the thin film transistor, wherein the semiconductor apparatus is characterized by the fact that a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the semiconductor thin film forming the one of the electrodes of the signal storage capacitor in the pixel is the semiconductor thin film of the 4th, the 5th, the 6th, the 7th, the 8th or the 9th aspects of the invention.

[0045] A 35th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel and one of the electrodes of a signal storage capacitor in the pixel is formed of a semiconductor thin film in the same layer as an active layer of the thin film transistor, wherein the method is characterized by the fact that a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the method of fabricating the semiconductor thin film of the 10th, the 11th, the 12th, the 13th, the 14th or the 15th aspects of the invention is applied to fabrication of the semiconductor thin film forming the one of electrodes of the signal storage capacitor in the pixel.

[0046] A 36th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor thin film or a semiconductor apparatus of the 10th, the 11th, the 12th, the 13th, the 14th, the 15th, the 27th, the 28th, the 29th, the 30th or the 35th aspect of the invention, wherein the method is characterized by the fact that the semiconductor thin film or the semiconductor apparatus is fabricated using an apparatus in which at least a film forming apparatus for forming a semiconductor thin film and a laser crystallizing apparatus are connected to each other by a transfer apparatus having an evacuating apparatus.

[0047] In addition to the characteristics of the method of fabricating the semiconductor thin film or the semiconductor apparatus of the 10th, the 11th, the 12th, the 13th, the 14th, the 15th, the 27th, the 28th the 29th, the 30th or 35th aspects of the invention, a 37th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor thin film or a semiconductor apparatus which is characterized by the fact that the semiconductor thin film or the semiconductor apparatus is fabricated using an apparatus in which at least a film forming apparatus for forming a semiconductor thin film, a film forming apparatus for forming an insulation film and a laser crystallizing apparatus are connected to each other by transfer apparatuses each having an evacuating apparatus.

[0048] In addition to the characteristic of the 36th or the 37th aspects of the invention, a 38th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor thin film or a semiconductor apparatus which is characterized by the fact that the atmosphere of the transfer apparatus is maintained in a vacuum below 10-5 torr or an atmosphere of an inert gas such as nitrogen, helium, neon, argon or the like.

[0049] In addition to the characteristics of the 10th, the 11th, the 12th, the 13th, the 14th, the 15th, the 27th, the 28th, the 29th, the 30th or the 35th aspects of the invention, a 39th aspect in accordance with the present invention is directed to a method of fabricating a semiconductor thin film or a semiconductor apparatus which is characterized by the fact that the semiconductor thin film or the semiconductor apparatus is fabricated using an in-line type apparatus in which at least a film forming portion for forming a semiconductor thin film, a laser crystallizing portion and a transfer portion are placed in a single chamber.

BRIEF DESCRIPTION OF DRAWINGS

[0050] FIGS. 1(A) to 1(D) are diagrammatic views illustrating the sectional structure and the plane structure of a polycrystalline silicon thin film fabricated in accordance with the present invention.

[0051]FIG. 2 is a graph illustrating method of calculating an average roughness of a surface when the surface is analyzed by a two-dimensional sectional structure.

[0052] FIGS. 3(A) and 3(B) are schematic diagrams showing a film forming apparatus and a laser crystallizing apparatus, respectively, used in the fabricating process to which the method of fabricating the polycrystalline silicon thin film in accordance with the present invention is applied.

[0053] FIGS. 4(A) to 4(E) are cross-sectional diagrams illustrating a fabricating process for polycrystalline silicon in accordance with the present invention.

[0054] FIGS. 5(A) to 5(C) are cross-sectional diagrams showing a fabricating process for the production of a semiconductor thin film in which crystal grain boundaries are positioned.

[0055]FIG. 6 is a schematic diagram showing a semiconductor thin film fabricating apparatus of an inline type which is used at the time when the present invention is applied to fabrication of a semiconductor device.

[0056] FIGS. 7(A) to 7(D) are cross-sectional diagrams showing the fabricating process to which the method of fabricating the polycrystalline silicon thin film in accordance with the present invention is applied.

[0057]FIG. 8 is a graph comparing the gate voltage versus drain current characteristics of a polycrystalline silicon thin film transistor in accordance with the present invention and a thin film transistor fabricated through a conventional fabricating method.

[0058]FIG. 9 is a schematic circuit diagram showing the construction of an embodiment of an active matrix type liquid crystal display apparatus in accordance with the present invention.

[0059]FIG. 10 is a diagrammatic view showing the plane structure of one pixel in an embodiment of an active matrix type liquid crystal display apparatus in accordance with the present invention.

[0060]FIG. 11 is a cross-sectional view showing the structure of one pixel in the embodiment of the active matrix type liquid crystal display apparatus in accordance with the present invention.

[0061]FIG. 12(A) is plan view and FIG. 12(B) is a sectional view of a pixel in an active matrix type liquid crystal display apparatus in which the polycrystalline silicon in accordance with the present invention is used for an electrode on one side of a signal accumulating capacitor in the pixel.

[0062] FIGS. 13(A) and 13(B) are layout diagrams showing the construction of a peripheral circuit containing liquid crystal display apparatus to which the present invention is applied.

[0063] FIGS. 14(A) to 14(C) are cross-sectional is a view showing an example of a laser irradiation method in accordance with the present invention.

[0064] FIGS. 15(A) and 15(B) are cross-sectional views of respective embodiments of thin film transistors in a peripheral circuit containing liquid crystal display apparatuses to which the present invention is applied.

[0065]FIG. 16 is a cross-sectional view showing a solar cell to which the present invention is applied.

[0066]FIG. 17 is a schematic diagram showing an embodiment of a semiconductor thin film fabricating apparatus used at the time when the present invention is applied to fabrication of a solar cell.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0067] Embodiments of the present invention will be described below with reference to the accompanying drawings.

[0068] Initially, a first embodiment in which the present invention is applied to fabrication of a polycrystalline silicon thin film will be described below with reference to the drawings. FIGS. 1(A) and (B) are a plan view and a sectional view, respectively, showing the crystal structure of polycrystalline silicon formed on a glass substrate 1 and a lower base insulation film 2 through a method of the present invention. FIGS. 1(C) and (D) are a plan view and a sectional view, respectively, showing the crystal structure of polycrystalline silicon having an average crystal grain size of 210 nm fabricated through a conventional laser crystallization method. The film thickness of the polycrystalline silicon in both examples is 60 nm. It can be understood from the plane structure of the polycrystalline silicon that is formed in accordance with the present invention, as shown in FIG. 1(A), that the average crystal grain size is as large as 530 nm, and from the cross-sectional view of FIG. 1(B) that projections are hardly produced at the crystal grain boundaries. On the other hand, in the polycrystalline silicon that is formed according to the conventional fabrication method, a projection having a level of height equal to the thickness of the film is produced at the crystal grain boundary. In accordance with the present invention, the size of a crystal grain is defined as the size of a pattern whose periphery is surrounded by etched grain boundaries appearing when the surface of the polycrystalline silicon is treated with SECCO etching solution to selectively etching the crystal grain boundaries. This pattern can be observed using an analysis apparatus, such as a scanning electron microscope (SEM), an atomic force microscope (AFM), a scanning tunneling microscope (STM) or the like. Further, the grain size of each crystal grain is defined by the diameter of a circle having an area equal to the area of each crystal grain, and the average crystal grain size 1a of an arbitrary region (an area S) containing m crystal grains is defined by the following equation. In accordance with the present invention, in the case of using a SEM, the area S of the region to obtain an average crystal grain size is defined as the sum of areas of crystal grains each of which is photographed at a magnification capable of checking the size of a crystal grain and each of which is photographed so that the whole grain boundary falls within the field of view without being cut out of the field of view. In a case where there are a plurality of fields of view, the area S of the region is defined as the total sum of the sums of areas of crystal grains each of which falls within the individual field of view in the whole grain. In the case of using an AFM or a STM, the area S of the region is defined as the sum of areas of crystal grains, each whole grain boundary of which falls within the arbitrary measuring field.

1a=2X((S/m)/π)^(1/2)

[0069] In accordance with the present invention, the shape of each crystal grain is irregular because the polycrystalline silicon is formed by laser crystallization. However, since the polycrystalline silicon isotropically grows from a generated crystal seed in a direction parallel to the substrate when the melted silicon is crystallized, the shape of the polycrystalline silicon crystal does not become a complex dendrite which can be observed in polycrystalline silicon formed through a solid phase growth method. From observation of crystal grains after treating a surface of the polycrystalline silicon with SECCO etching solution, it was found that, in the polycrystalline silicon that is formed in accordance with the present invention, at least more than 50% of the crystal grains satisfied the relation Ln≦4πRn. Therein, Rn=(Sn/π)^(1/2), Sn is a surface area of an arbitrary crystal grain, and Ln is a circumferential length on the surface of the arbitrary crystal grain. From the above relation, it can be understood that the volume of the crystal grain boundary of the polycrystalline silicon in accordance with the present invention is smaller than that of the polycrystalline silicon film prepared through a solid phase growth and composed of crystal grains for which the above relation generally does not hold, and that the polycrystalline silicon formed in accordance with the present invention is a high-quality crystalline semiconductor having a small defect density over the whole silicon film. Further, from observation of a cross section of the polycrystalline silicon of the present invention using a transmission electron microscope (TEM), it was found that more than 70% of all the crystal grains continuously extended from an interface between the semiconductor layer and a base layer to the semiconductor surface without a discontinuity at some midpoint. Because there are few regions in the film where plural crystal grains are stacked up in the direction of the film thickness, the polycrystalline silicon in accordance with the present invention is a high-quality polycrystalline silicon having less defects caused by crystal grains extending in the lateral direction of the substrate. It was found from measurement of the surface of the semiconductor film using an atomic force microscope (AFM) that the average roughness of the surface was 2 nm. Therein, the average roughness of the surface with respect to the present invention means an arithmetic average roughness (Ra), and in a case of three-dimensionally analyzing the surface form of the semiconductor, the average roughness of the surface is a value obtained by dividing a volume of a portion that is surrounded by a quadric surface of the surface form and a plane at the average level of the surface form by the measured area. In accordance with the present invention, when an analyzing apparatus that is capable of three-dimensionally analyzing the surface form, such as an AFM, a scanning tunneling electron microscope (STM) or the like, is used for analyzing a measured area, the measured area is an arbitrary region of the semiconductor surface having a size larger than an analysis limit area which is analyzable by the analyzing means. On the other hand, in the case of analyzing a surface form of the two-dimensional cross-sectional structure of a semiconductor, the average roughness of the surface is a value obtained by dividing an area of a portion surrounded by a quadric curve of the surface form and a line in the average level of the surface form by the measured length, as shown in FIG. 2. The cross-sectional structure can be observed by a photograph taken by a TEM or a high-resolution scanning electron microscope (SEM). Further, the cross-sectional structure can be observed by scanning the measuring needle of an AFM or an STM once. In accordance with the present invention, when an electron microscope, such as an AFM or an STM, is used as an analyzing means, the region of measured length for calculating the average roughness is a field of view or plural fields of view of the electron microscope in a magnitude capable of calculating the roughness. When an AFM or STM is used, the measured length is an arbitrary region of the semiconductor surface having a length longer than an analysis limit length. In accordance with the present invention, the method of calculating the average roughness may employ either a method of calculating from a three-dimensional form or a method of calculating from a cross-sectional form. Letting the average height of the plane be the X-Y plane, the longitudinal direction be the Z axis, and the curve of the measured surface form be z=f(x, y), when a three-dimensional form is observed, the average roughness Ra can be expressed by the following equation:

Ra=(1/(Lx·Ly))X∫ ^(Lx) ₀∫^(Ly) ₀ f(x, y)dxdy

[0070] where Lx is a measured length in the X direction, and Ly is a measured length in the Y direction.

[0071] On the other hand, Letting the average height of the line be on X axis, the longitudinal direction be on Y axis, and the curve of the measured surface form be y=f(x), when the cross-sectional form is observed, the average roughness Ra can be expressed by the following equation:

Ra=(1/Lx)X ∫ ^(Lx) ₀ f(x)dx,

[0072] where Lx is a measured length in the X direction.

[0073] Further, from observation of the polycrystalline silicon film in accordance with the present invention by X-ray diffractometry, it was found that the crystal plane of the silicon film was oriented to mainly the (1. 1. 1) plane. The polycrystalline silicon in accordance with the present invention is very useful for an active layer of a thin film transistor and a semiconductor layer of a solar cell because the crystal grain size is as large as 530 nm and the roughness is as even as 2 nm; and, accordingly, the performance of the thin film transistor or the solar cell can be largely improved by using the polycrystalline silicon.

[0074] A method of fabricating the polycrystalline silicon film in accordance with the present invention will be described below. FIG. 3(A) shows a semiconductor thin film fabricating apparatus used in the process according to the present invention, which apparatus comprises a substrate loading chamber L, an insulation film forming chamber R1, an intrinsic semiconductor film forming chamber R2 and a laser processing chamber LA arranged so as to surround a transfer chamber T, which is composed of a substrate transfer robot and an evacuating pump, and the respective chambers are connected to the transfer chamber T. A substrate can be transferred without being exposed to the atmosphere between each of the film forming chambers and the laser processing chamber through the transfer chamber T, in which the vacuum level is maintained higher than 10-5 torr. The polycrystalline silicon film in accordance with the present invention also can be fabricated by an apparatus having a layout in which a substrate loading chamber L, an insulation film forming chamber R1, an intrinsic semiconductor film forming chamber R2 and a laser processing chamber LA are arranged in line, and a transfer chamber T composed of a substrate transfer robot and an evacuating pump is arranged along the four chambers, as shown in FIG. 3(B).

[0075] Initially, a base insulation film 2 having a thickness of 300 nm formed of silicon oxide is formed on a glass substrate 1 while maintaining the substrate at a temperature below 350° C. through plasma assisted chemical vapor deposition (PECVD) using tetra-ethyl ortho-silicate (TEOS) and oxygen as raw materials, as shown in FIG. 4(A). Next, an amorphous silicon film 3 having a thickness of 35 nm and a combined hydrogen concentration in the film of 7% is formed while maintaining the substrate at a temperature below 400° C. using mono-silane and hydrogen as raw materials in the intrinsic semiconductor film forming chamber R2, as shown in FIG. 4(B). Next, the glass substrate 1 is transferred from the intrinsic semiconductor film forming chamber R2 to the laser processing chamber LA through the transfer chamber T while maintaining a vacuum. In the laser processing chamber LA, the substrate temperature is kept at 350° C. using a heater. Then, as shown in FIG. 4(C), a polycrystalline silicon 5 is formed by irradiating a Xe—Cl excimer laser beam 4 having a line beam shape by selecting an irradiation pitch so that the preceding laser beam and the following laser beam are overlapped by 90% with respect to each other (an irradiation pitch equivalent to performing 10 times of laser irradiation on any position) and increasing the energy density of the laser beam from 200, 300 to 380 mJ/cm² stepwise. Because the laser is irradiated in multi-steps, the amorphous silicon film 3 is dehydrogenated while the weak energy laser is being irradiated. Therefore, the amorphous silicon film 3 can be crystallized without damaging the film even if the combined hydrogen concentration in the film is above 3%. If the combined hydrogen concentration in the film is below 10%, a sufficient number of steps of laser irradiation is three or less. Therefore, the fabrication time can be shortened, and, accordingly, the throughput can be improved. After completion of the laser irradiation, the glass substrate 1 is transferred from the laser processing chamber LA to the intrinsic semiconductor film forming chamber R2 through the transfer chamber T while maintaining a vacuum. Then, as shown in FIG. 4(D), an amorphous silicon film 3 having a thickness of 25 nm and a combined hydrogen concentration in the film of 7% is formed while maintaining the substrate at a temperature below 400° C. using mono-silane and hydrogen as raw materials in the intrinsic semiconductor film forming chamber R2. Next, the glass substrate 1 is transferred from the intrinsic semiconductor film forming chamber R2 to the laser processing chamber LA through the transfer chamber T while maintaining a vacuum. Then, as shown in FIG. 4(E), a large grain size polycrystalline silicon 6 is formed by irradiating a Xe—Cl excimer laser beam 4 having a line beam shape by selecting an irradiation pitch so that the preceding laser beam and the following laser beam are overlapped by 90% with respect to each other and by increasing the energy density of the laser beam from 200, 300 to 520 mJ/cm² stepwise. Thus, fabrication of the polycrystalline silicon is completed. As described above, according to the present invention, it is possible to form a high-quality polycrystalline silicon film having a film thickness of 60 nm, an average size of the crystal grains of 530 nm and an average surface roughness of 2 nm on an economical glass substrate. Accordingly, the fabrication cost of the high-quality polycrystalline silicon can be reduced.

[0076] The laser crystallization mechanism of the present invention will be described below. The inventors have found that a polycrystalline silicon film having an average surface roughness below 5 nm and small projections and an average crystal grain size above 300 nm could be fabricated by irradiating laser light in three steps from low energy to high energy on an amorphous silicon film having a film thickness below 40 nm. This was determined from the fact that the crystal growth during laser irradiation in the third step was mainly crystal growth of secondary grain growth by melt-combining of crystal grains having a grain size of 100 to 200 nm which had been produced from isotropic growth by melting and solidifying by the laser irradiation up to the second step, and not that the crystal growth during laser irradiation in the third step was crystal growth of melted silicon in the lateral direction which produced the projections. The amorphous silicon 3 of the first layer crystallized first is a film as thin as 35 nm, and the polycrystalline silicon 5 of the first layer, having an average roughness in the surface of 5 nm and an average crystal grain size of 400 nm, is formed by the laser crystallization method of three step irradiation in accordance with the present invention. When the laser crystallization for the second layer is performed, the film of the first layer is already crystallized to polycrystalline silicon, and, consequently, the melting point becomes higher than that of amorphous silicon. Therefore, the melted zone of the polycrystalline silicon 5 of the first layer during the laser crystallization for a second layer is only in the vicinity of the boundary zone with the silicon in the second layer. The film thickness of the amorphous silicon in the second layer is 25 nm, and, accordingly, the silicon melted during the laser crystallization for the second layer is the whole silicon in the second layer and only the very thin zone in the upper layer of the silicon of the first layer. Therefore, the thickness of the silicon melted during the second laser crystallization is thinner than the thickness of the silicon melted during the first laser crystallization. It is believed that the grain size of the semiconductor thin film is likely to grow larger by the secondary grain growth caused by melt-combining with an adjacent crystal grain by plural times of laser irradiation, as the thickness of the semiconductor thin film becomes thinner. The theoretical explanation is reported in the Applied Physics Letter, Vol. 44, No. 6, 19894, p602. The non-melted polycrystalline silicon 5 in the lower layer is heated up to 1000° C. or more by heat conduction by contact with the melted silicon and absorption of the laser light. Since this portion serves as a heat reservoir when the melted silicon in the upper layer is crystallized, the cooling speed is slowed down, and, accordingly, the crystallization speed is decreased to form the large grain sized polycrystalline silicon 6 having an average crystal grain size of 530 nm. This grain size is larger than the average crystal grain size of 210 nm, which is obtained from laser-crystallizing a single amorphous silicon layer having a thickness of 60 nm, which is equal to the sum of the thickness of the silicon films of the first layer and the second layer, similar to the conventional method. In order to improve the effect of the heat reservoir, it is preferable that the thickness of the silicon of the first layer is set to a value larger than the thickness of the silicon in the second layer. Further, since the secondary grain growth obtained by melt-combining with the adjacent crystal grain occurs when the semiconductor layer is in a high temperature state above 600° C. even if the semiconductor layer is not melted, growth of the crystal grains in the heated polycrystalline silicon of the first layer by the secondary grain growth and the melt-combination between the growing crystal grains of the first layer and the crystal grains under growing by solid crystallization occur at the same time. As a result, in the produced large grain sized polycrystalline silicon 6, at least more than 70% of the crystal grains continuously extend from the interface between the semiconductor layer and a base insulation layer 2 to the semiconductor surface without discontinuity at some midpoint. Therefore, since the ratio of the region where the crystal grains overlap in the film-thickness direction is decreased, the number of defects caused by the crystal grain boundaries in the polycrystalline silicon become small, and, accordingly, the characteristic of the semiconductor can be improved. Further, since the mechanism of crystal grain growth obtained in the first and the second layers is the secondary grain growth by melt-combining of the crystal grains, as described above, which is not growth in the lateral direction which tends to produce a projection on the surface, the height of the projection produced during laser crystallization becomes lower than the height of the projection which is obtained from laser-crystallizing a single amorphous silicon layer having a thickness equal to the sum of the thickness of the silicon films of the first layer and the second layer, similar to the conventional method, and, consequently, it is possible to suppress the occurrence of the unevenness on the polycrystalline silicon surface. Furthermore, even if the projections are formed in the polycrystalline silicon of the first layer, the projections are melted first in the polycrystalline silicon of the first layer when the amorphous silicon of the second layer is laser crystallized, because the crystal quality of the projections is bad and the melting point is as low as that of amorphous silicon. Therefore, the projections on the surface are suppressed over the whole polycrystalline silicon film so as to make the surface even. As a result, the average roughness of the surface of the polycrystalline silicon fabricated according to the present invention becomes 2 nm, and the greater evenness increases the applicability of the polycrystalline silicon to various kinds of semiconductor devices, such as a thin film transistor and so on, as will be described in connection with the following embodiments. The film thickness of the polycrystalline silicon 6 in the above-described embodiment is 60 nm. However, if the film thickness of the polycrystalline silicon 6 is below 40 nm, a small amount of metallic ions and oxygen, nitrogen, and a carbon impurity contained in the base glass substrate 1 and the base insulator film 2 are diffused into the polycrystalline silicon 6 by heat during laser irradiation to decrease the quality of the film, not only in the lower portion, but also in the upper portion of the polycrystalline silicon. From this viewpoint, a thickness of 60 nm is preferable. It is advantageous for controlling the film thickness and preferable from the viewpoint of application to a semiconductor device, such as a thin film transistor, that the film thickness of the polycrystalline silicon 6 is above 40 nm. On the other hand, in regard to the upper limit of the film thickness, a film thickness below 100 nm is preferable from the viewpoint of the ability to cover silicon steps of metal or insulation to be deposited on the island-shaped polycrystalline silicon 6 when a semiconductor device, such as a thin film transistor or a liquid crystal display apparatus, is fabricated. This upper limit is not applied in a case where the polycrystalline silicon is applied to a semiconductor apparatus requiring a thick semiconductor film such as a solar cell or the like. In accordance with the present invention, by repeating the steps of forming the amorphous silicon film and crystallizing the amorphous silicon film by irradiating laser light at least two times, a polycrystalline silicon having a film thickness above 40 nm and below 100 nm, an even surface and a large crystal grain size can be easily fabricated. The film thickness of the amorphous silicon of the first layer and the film thickness of the amorphous silicon of the second layer are set to 35 nm and 25 nm in the above embodiment, respectively, but are not fixed to these values. If the film thickness of the first layer is thicker than the thickness of the second layer and the total thickness of the first and the second layers is above 40 nm, the values of film thickness may be varied depending on the film quality of each semiconductor and the kind of semiconductor apparatus to which the semiconductor is applied. In accordance with the present invention, since the substrate is transferred from the film forming chamber to the laser processing chamber while maintaining a vacuum, no concentration peak of silicon oxide will exist on the surface of the polycrystalline silicon 5 of the first layer during film-forming of the amorphous silicon of the second layer, and, consequently, the characteristics of the polycrystalline silicon are not deteriorated by diffusion of oxygen atoms in the melted silicon during laser-crystallizing of the amorphous silicon of the second layer. Of course, no concentration peak of oxygen exists in the polycrystalline silicon. In addition, since no silicon oxide layer exists on the surface of the polycrystalline silicon 5 of the second layer, and, consequently, oxygen atoms do not diffuse from the surface to the inside during being melted at the time of laser crystallization, the characteristic of the polycrystalline silicon can be improved. As described above, according to the present invention, it is possible to form a polycrystalline silicon film having a film thickness above 40 nm, an even surface having an average surface roughness of 2 nm, an average size of the crystal grains above 500 nm and a good semiconductor characteristic with less oxygen concentration in the film on an economical glass substrate.

[0077] In the above embodiment, although the silicon oxide base film under the silicon film is an even film, the shape of the base film may be patterned through the photo-lithography method and the wet or dry etching method. As shown in FIGS. 5(A) and 5(B), a 10 nm step was provided on a base film 2 made of silicon oxide, and the steps of forming of an amorphous silicon film by the PECVD process and laser crystallization was repeated twice through the same process as described above. In this case, the inventors found that a crystal grain boundary was produced at the step portion, as shown in FIG. 5(C). Further, it was also found that the crystal grains in contact with the step on the base insulation film located at the lower position of the step were oriented mainly in the (1, 1, 0) plane or the (1, 0, 0) plane. Although the cause of occurrence of these phenomena is unknown, the position producing deterioration at the crystal grain boundary of the electric characteristic of the polycrystalline silicon could be controlled by changing the shape of the base insulator film. By doing so, it was possible to obtain a high-quality polycrystalline silicon having an average crystal grain size above 500 nm and an average surface roughness of 2 nm, in which at least a part of the crystal grain boundaries were positioned.

[0078] Further, in accordance with the present invention, since the substrate is heated during laser crystallization, the heating time of the substrate after transferred between the laser crystallization process and the semiconductor thin film forming process can be shortened. Therefore, the throughput of the fabrication of the crystalline semiconductor thin film can be improved. Further, since the cooling speed of the semiconductor melted by laser irradiation can be made slow by heating the substrate during laser crystallization, the crystal grain size of the crystalline semiconductor thin film can be made large, and, consequently, the quality of the crystal can be improved. In the present embodiment, although the film forming temperature of the base insulation film, the film forming temperature of the amorphous silicon and the base temperature during laser crystallization are set to 350° C., 400° C. and 350° C., respectively, it is possible that these temperatures need not be fixed, but may be varied depending on the film quality of the insulation film or the semiconductor or the performance of the target semiconductor apparatus. However, when a glass substrate is used for the substrate and silicon is used for the semiconductor, these temperatures are preferably set to a value between 200° C. and 500° C. In the apparatus for fabricating the polycrystalline silicon used in the present embodiment, each of the film forming chambers and the laser crystallizing chamber and the substrate loading chamber are connected with the transfer chamber T, which is composed of a substrate transfer robot and an evacuating pump, as shown in FIGS. 3(A) and 3(B). However, the polycrystalline silicon in accordance with the present invention can be fabricated by an in-line type semiconductor fabricating apparatus in which each of the film forming parts, a laser crystallizing part and a transfer part are arranged in a single chamber, as shown in FIG. 6. By using an in-line type semiconductor fabricating apparatus which is low in manufacturing cost, the cost of equipment can be suppressed, and, consequently, the semiconductor apparatus can be fabricated with a low cost. In the present, embodiment the substrate is transferred by maintaining the transfer system at a high vacuum below 10⁻⁵ torr. However, the substrate may be transferred under an atmosphere of an inert gas, such as nitrogen, helium, neon, argon or the like, because the present invention requires that a natural oxide film not be formed on the silicon surface after forming the amorphous silicon film or after laser crystallizing the amorphous silicon. In this regard, the transfer under an atmosphere of an inert gas can attain the same effect as the transfer in a vacuum.

[0079] In the above embodiment, the Xe—Cl excimer laser is used for crystallizing the silicon film. However, various kinds of excimer lasers, such as a Kr—F excimer laser, an Ar—F excimer laser or the like, or a continuous-wave laser, such as an Ar ion laser and the like, or an energy beam, such as an electron beam or the like, may be used for crystallizing regardless of the kind of device in principle, if it can crystallize the silicon film.

[0080] Further, in the above embodiment, although the present invention is applied to amorphous silicon, the present invention can be applied to fine-crystalline silicon, polycrystalline silicon, impurity-doped silicon, silicon-germanium (SiGe), germanium (Ge) and so on, regardless of the kind of semiconductor, if it can be crystallized by heating using a laser. Further, in the above embodiment, the film forming apparatus is of the plasma assisted chemical vapor deposition type. However, a low-pressure chemical vapor deposition type (LPCVD), a sputtering type, an ion beam type, an atom beam type, a molecule beam type, a spin-coat type or a vapor deposition type film forming apparatus may be employed regardless of the type, if it can be connected to the transfer chamber T and can transfer the substrate between the transfer chamber and the laser processing chamber LA without exposing the substrate to the atmosphere or while maintaining a vacuum. Furthermore, in the above embodiment, the substrate used is made of glass. However, a substrate made of an organic resin, such as a substrate made of polyimide, polyamide or polyester can be used if the film forming temperatures of the base insulator film 2 and the amorphous silicon 3 are reduced to a value lower than 300° C.

[0081] The second embodiment of fabrication of a copalanar type thin film transistor to which the present invention is applied will be described below.

[0082] As shown in FIG. 7(A), a large grain size polycrystalline silicon 6, which is selected to be an active layer of a thin film transistor, is formed on a glass substrate 1 having a base insulator film 2 using a method similar to that in the first embodiment. As shown in FIG. 7(B), after forming the polycrystalline silicon 6 into an island-shape through the photo-lithographic method and the dry etching method, a gate insulation film 7, having a film thickness of 100 nm, is formed by the plasma assisted chemical vapor deposition method using TEOS and oxygen as raw materials. Then, after forming a niobium (Nb) film having a film thickness of 250 nm through the sputtering method, a gate electrode 8 is formed by processing the niobium film using the photo-lithographic method and the dry etching method. Next, as shown in FIG. 7(C), after implanting the impurity phosphorus (P) into a region of the active layer not overlapping with the gate electrode 8 using the ion implantation method, a source region 9 and a drain region 10 are formed by activating the impurity by heating the substrate at 500° C. for 2 hours using an electric furnace. Then, as shown in FIG. 7(D), after forming an inter-layer insulation film 11 having a film thickness of 500 nm through the plasma assisted chemical vapor deposition method using TEOS and oxygen as raw materials, contact holes are formed through the photo-lithographic method and the dry etching method. Finally, after forming a chromium-molybdenum alloy (Cr—Mo) film having a film thickness of 500 nm through the sputtering method, a gate electrode, a source electrode 12 and a drain electrode 13 are processed through the photo-lithographic method and the wet etching method. Thus, the thin film transistor is completed.

[0083] By using polycrystalline silicon having a large crystal grain size of 530 nm and an average surface roughness of 2 nm for the active layer, it was possible to fabricate a high-performance thin film transistor having a mobility of 300 cm²V·s which is largely improved compared to the mobility of 140 cm2V·s of a thin film transistor fabricated through the conventional method.

[0084]FIG. 8 is a graph which compares the gate voltage versus drain current characteristics of a polycrystalline silicon thin film transistor in accordance with the present invention with those of a thin film transistor having an active layer made of a polycrystalline silicon which is fabricated in the conventional manner, in which an amorphous silicon film having a film thickness of 60 nm formed through the plasma assisted chemical deposition method is heated at 450° C. under a nitrogen atmosphere to perform dehydrogenating treatment, and then the amorphous silicon is laser crystallized. It is clear from FIG. 8 that the ON current in the polycrystalline silicon thin film transistor of the present invention is increased by the effects of an increase in the crystal grain size and a decrease in the roughness (projections) of the active layer film. Further, because the electric field concentration in the projection is suppressed by the even surface of the active layer of the polycrystalline silicon 6 in accordance with the present invention, the dielectric breakdown voltage of the gate insulator film 7 is largely increased from 4 MV/cm to 7 MV/cm to improve the withstand voltage characteristic, and the reliability relative to hot carriers is also improved. Furthermore, since the thickness of the gate insulation film can be made thinner, that is, below 80 nm, compared to that in the conventional method, the thin film transistor can be driven by a lower voltage, and, accordingly, the power consumption of a semiconductor apparatus using the thin film transistor can be reduced. By using the polycrystalline silicon in accordance with the present invention in an active layer of a thin film transistor, the film thickness of the gate insulation film and the film thickness of the active layer can be set so that a ratio of the film thickness of the gate insulation film to the film thickness of the active layer becomes a value smaller than 8/6. Further, by optimizing the film quality of the gate insulation film, the thickness of the gate insulation film can be made thinner, and, accordingly, the thin film transistor can be driven by a lower consumed power.

[0085] Although application of the present invention to a coplanar type thin film transistor has been described in the above embodiment, the present invention can be applied to an inverse stagger type or a normal stagger type thin film transistor regardless of the type of the thin film transistor.

[0086] A third embodiment of an active matrix type liquid crystal display apparatus to which the thin film transistors in accordance with the present invention are applied will be described below.

[0087]FIG. 9 is a circuit diagram showing the construction of the embodiment of the active matrix type liquid crystal display apparatus in accordance with the present invention. Referring to the figure, a thin film transistor (TFT) is provided in each of a plurality of liquid cells (LC) arranged in the form of a matrix, and each of the liquid cells is driven by switching operation of the TFT. Therein, a gate voltage is sequentially applied to gate lines G1 to GM of electrodes commonly led out from individual gates of the TFTs aligned in the lateral direction on a glass substrate 1 to switch on the gates from gate line to gate line. On the other hand, a data voltage for each switched-on gate line is sequentially applied to drain lines D1 to DN of electrodes commonly led out from individual drains of the TFTs aligned in the perpendicular direction to be supplied to each of the liquid cells.

[0088]FIG. 10 is a plan view showing the plane structure of one pixel composed of one liquid cell and one TFT. Further, FIG. 11 shows the cross-sectional structure along the fine X-X′ of FIG. 10. The pixel is composed of a TFT formed near a cross point of the drain wire D and the gate wire G and the liquid cell LC connected to the TFT through a source electrode 12. The sectional structure of the TFT is nearly equal to that of the second embodiment. The structure can be obtained through the fabricating method described in the second embodiment, but points different from the above-described process are as follows. Ion implantation at the time of forming the source-drain region is separately performed twice, and a locally doped drain (LDD) region having a lower impurity concentration is provided in the source-drain region in contact with the active layer in order to reduce the OFF current. Further, the gate wire G is formed by processing film-forming and etching together with the gate electrode 8. An inter-layer insulator film 14 made of SiN is formed after forming the source and the drain electrodes 12, 13. After processing this workpiece to bore a contact hole to the source electrode 12, an indium-tin oxide film (ITO) is formed and patterned to form a pixel electrode 15. Parts other than the TFT, such as the liquid crystal, will be described below.

[0089] TN type liquid crystal 16 is filled between the glass substrate 1 having the TFT formed thereon and a glass substrate 17 (an opposite substrate) opposite to the glass substrate 1. A black matrix 18 for cutting off unnecessary light and an opposite electrode 19 made of ITO are formed on the opposite substrate. The liquid crystal is driven by a voltage between the opposite electrode 19 of the opposite substrate 17 and the pixel electrode 15 of the TFT substrate, and an image is displayed on the matrix of the pixels by changing the display brightness pixel-by-pixel. A polarizing plate 20 for polarizing light is attached onto each of the glass substrates 1, 17. By orientating the polarization axes of these two polarizing plates in orthogonal or parallel directions relative to each other, a normally black display mode or a normally white display mode is obtained, respectively. Polarizing films 21 for polarizing the liquid crystal are applied onto the surfaces in contact with the liquid crystal, that is, onto the surface of the inter-layer insulation film 14 and the pixel electrode in the glass substrate 1 side and onto the surface of the opposite electrode 19 in the opposite substrate 17 side. After applying the polarizing film, the surface of the polarizing film is processed by the lapping method to add anisotropy for orientating the liquid crystal molecules to the polarizing film. A back light serving as a light source is placed on the substrate 1 side to give brightness to the display.

[0090] By using the TFTs fabricated as described above in accordance with the present invention for the driving elements of the display part pixels of the active matrix type liquid crystal display apparatus, the TFT can be made small because the grain size of the active layer polycrystalline silicon is large and the mobility is large. Therefore, the opening ratio of the pixel is increased, and, accordingly, the power of the back light can be reduced by that amount, whereby a reduction in the power consumption of the liquid crystal display apparatus can be attained. Further, since the surface of the TFT active layer is made even and the projections are eliminated, the thickness of the gate insulation film can be made thinner than 80 nm. Therefore, the TFT can be driven by a low voltage, and, accordingly, low power consumption in the liquid crystal display apparatus can be attained. Furthermore, since the surface is made even and, accordingly, the characteristic inside the polycrystalline silicon is made uniform, display defects caused by non-uniformity of the characteristic of the polycrystalline silicon TFT can be eliminated.

[0091] As shown by FIG. 12(A) and FIG. 12(B), which is a cross-sectional view taken on the plane of the dashed line X-X′ in FIG. 12(A), in a case where a signal storage capacitor of the pixel is formed by sandwiching a silicon oxide film in the same layer of the gate insulation film with an n-type polycrystalline silicon formed by doping phosphorus into the polycrystalline silicon in the same layer of the polycrystalline silicon 6 of the active layer and the common wire formed of a metallic thin film in the same layer of the gate wire, if the polycrystalline silicon in accordance with the present invention is used, the film thickness of the silicon oxide film can be made thin because the unevenness on the surface is very small and, consequently, there is no possibility of occurrence of dielectric breakdown caused by electric field concentration at a projection. Because of the distance between the electrodes, the capacitance of the signal storage capacitor is increased, and, consequently, the area of the electrode can be reduced and the opening ratio of the pixel can be increased. Therefore, low power consumption of the liquid crystal display apparatus can be attained by reducing the brightness of the back light.

[0092] Further, by constructing the peripheral circuit for driving the display part using the TFTs in accordance with the present invention, as shown in FIG. 13(A), a small-frame size and low-cost liquid crystal display apparatus incorporating a peripheral circuit can be manufactured by eliminating the driver LSI. Further, as shown in FIG. 13(B), by incorporating not only the display part driving circuit, but also a memory, a micro processing unit (MPU) and another information processing unit formed through micro-processing in the periphery of the display part, an advanced liquid crystal display apparatus can be obtained by adding a communication function and a calculating function to the liquid crystal display apparatus.

[0093] Furthermore, after crystallizing an amorphous silicon in the first layer as shown in FIG. 14(A), an amorphous silicon film 3 in the second layer is formed without exposing the atmosphere, as shown in FIG. 14(B), and then a part of the region of the amorphous silicon 3 in the second layer may be intentionally left in the amorphous state without irradiating laser light on that region, as shown in FIG. 14(C). Then, as shown in FIG. 15(A), in the polycrystalline silicon/amorphous silicon region where the amorphous silicon in the second layer has been not irradiated, a display, part is provided to form a coplanar type TFT. In the polycrystalline silicon/polycrystalline silicon region where the amorphous silicon in the second layer has been laser crystallized, a peripheral circuit part is provided to form a copalanar type TFT of CMOS structure for driving the circuit. By doing so, because the active layer of the display part TFT becomes high resistance amorphous silicon, the OFF current is reduced, and, accordingly, there is no need to form an offset structure or a lightly doped drain (LDD) structure, which is necessary when the display part TFT is constructed using the polycrystalline silicon TFT. Therefore, the number of processes for fabricating the peripheral circuit incorporating the liquid crystal display apparatus is reduced by that amount, and, consequently, the throughput of the fabrication is improved and the cost is reduced.

[0094] The same effect can be obtained in a case where the TFT structure is of an inverse stagger type because a high resistance amorphous silicon exists between the polycrystalline silicon of the active layer and the source-drain region, as shown in FIG. 15(B). In contrast to the second embodiment, in fabricating the polycrystalline silicon TFT described with reference to FIGS. 14(A) to (C) and FIG. 15(A) and 15(B), when the source-drain region is formed, the impurity activation is performed using laser activation in order to prevent the amorphous region from being deteriorated and not using activation of thermal annealing using an electric furnace.

[0095] The present invention can be also applied to the formation of a semiconductor layer in a solar cell which is composed of a p-type, n-type and intrinsic polycrystalline silicon layers, as shown in FIG. 16. In accordance with the present invention, since the large grain sized and even polycrystalline semiconductor can be fabricated even if the thickness is increased, a solar cell having a high solar light converting efficiency above 15% can be fabricated. The solar cell can be fabricated with the fabricating apparatus shown in FIGS. 3(A), 3(B) or FIG. 6. However, in a case where the substrate is a long continuous substrate made of stainless steel or aluminum, the solar cell can be fabricated using an inline type fabricating apparatus as shown in FIG. 17. By using the inline type fabricating apparatus, the solar cell can be fabricated with a low cost. As described above, the present invention can be applied to all the semiconductor apparatuses using polycrystalline semiconductors in addition to thin film transistors.

[0096] According to the present invention, it is possible to fabricate a high-quality crystalline semiconductor having a film thickness above 40 nm, an average size of the crystal grains larger than 500 nm and an average roughness of the surface smaller than 5 nm on an economical glass substrate. Further, it is possible to improve the performance of the semiconductor apparatus using a semiconductor, such as a thin film transistor, a solar cell and an active matrix type liquid crystal display apparatus. 

What is claimed is:
 1. A crystalline semiconductor thin film fabricated by a laser crystallizing method, which is formed on a glass substrate, and has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm.
 2. A crystalline semiconductor thin film fabricated by a laser crystallizing method, which is formed on a glass substrate, and has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when a surface area of an arbitrary crystal grain is expressed by Sn and a circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2).
 3. A crystalline semiconductor thin film fabricated by a laser crystallizing method, which is formed on a glass substrate, and has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when a surface area of an arbitrary crystal grain is expressed by Sn and a circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2), and further when crystal structures on an arbitrary cross section of the crystalline semiconductor thin film are observed, at least more than 70% of the crystal grains continuously extend from an interface between the semiconductor layer and a base layer to the semiconductor surface without discontinuity at some midpoint.
 4. A crystalline semiconductor thin film fabricated by a laser crystallizing method, which is formed on a glass substrate, and has a film thickness thicker than 40 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm.
 5. A crystalline semiconductor thin film fabricated by a laser crystallizing method, which is formed on a glass substrate, and has a film thickness thicker than 40 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when a surface area of an arbitrary crystal grain is expressed by Sn and a circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2).
 6. A crystalline semiconductor thin film according to any one of claims 1, 2, 3, 4 and 5, wherein orientation of the semiconductor thin film is mainly (1.
 1. 1) plane.
 7. A crystalline semiconductor thin film according to any one of claims 1, 2, 3, 4, 5 and 6, wherein said semiconductor is silicon.
 8. A crystalline semiconductor thin film according to any one of claims 1, 2, 3, 4, 5, 6 and 7, wherein at least a part of crystal grain boundaries are positioned, and orientation of the part of crystal grains is mainly (1.
 0. 0) plane or (1.
 1. 0).
 9. A crystalline semiconductor thin film according to any one of claims 1, 2, 3, 4, 5, 6, 7 and 8, wherein the glass substrate is made of a no-alkali glass which has a softening point lower than 700° C.
 10. A method of fabricating a semiconductor thin film, the method comprises the steps of: forming an insulation film on a glass substrate; forming a semiconductor thin film on the insulation film; and continuously following the semiconductor thin film forming, crystallizing the formed semiconductor thin film by irradiating laser light without exposing to atmosphere, wherein the set of forming the semiconductor thin film and crystallizing the semiconductor thin film by irradiating laser light is repeated at least two times, and a method of irradiating laser light in each of the sets is that energy of the laser light is increased in steps from scanning of weak energy laser light to scanning of strong energy laser light.
 11. A method of fabricating a semiconductor thin film, the method comprises the steps of: forming an insulation film on a glass substrate; forming a semiconductor thin film on the insulation film; and continuously following the semiconductor thin film forming, crystallizing the formed semiconductor thin film by irradiating laser light without exposing to atmosphere, wherein the set of forming the semiconductor thin film and crystallizing the semiconductor thin film by irradiating laser light is repeated at least two times, and thickness of the film in an upper layer at semiconductor film forming is thinner than thickness of the film in a lower layer.
 12. A method of fabricating a semiconductor thin film according to any one of claim 10 and claim 11, wherein the film thickness of the semiconductor thin film formed in the first layer is within a range of 30 nm to 70 nm, and the film thickness of the semiconductor thin film formed in the second layer is within a range of 25 nm to 40 nm.
 13. A method of fabricating a semiconductor thin film according to any one of claims 10, 11 and 12, wherein the formed semiconductor thin film is silicon having a concentration of combined hydrogen in the film less than 10%.
 14. A method of fabricating a semiconductor thin film according to any one of claims 10, 11, 12 and 13, wherein temperature of the substrate during the laser crystallization is within a range of 200° C. to 500° C.
 15. A method of fabricating a semiconductor thin film according to any one of claims 10, 11, 12, 13 and 14, wherein the glass substrate used is a no-alkali glass and has a softening point lower than 700° C.
 16. A semiconductor apparatus containing a thin film transistor, wherein the thin film transistor is formed on a glass substrate, and a semiconductor thin film formed in an active layer of the thin film transistor through a laser crystallizing method has a thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm.
 17. A semiconductor apparatus containing a thin film transistor, wherein the thin film transistor is formed on a glass substrate, and a semiconductor thin film formed in an active layer of the thin film transistor through a laser crystallizing method has a thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when a surface area of an arbitrary crystal grain is expressed by Sn and a circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2).
 18. A semiconductor apparatus containing a thin film transistor comprising a semiconductor thin film, wherein the thin film transistor is formed on a glass substrate, and a semiconductor thin film formed in an active layer of the thin film transistor through a laser crystallizing method has a thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when a surface area of an arbitrary crystal grain is expressed by Sn and a circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2), and further when crystal structures on an arbitrary cross section of the crystalline semiconductor thin film are observed, at least more than 70% of the crystal grains continuously extend from an interface between the semiconductor layer and a base layer to the semiconductor surface without discontinuity at some midpoint.
 19. A semiconductor apparatus containing a thin film transistor, wherein the thin film transistor is formed on a glass substrate, and the semiconductor thin film according to any one of claims 4, 5, 6, 7, 8 and 9 is used in an active layer of the thin film transistor.
 20. A semiconductor apparatus containing a copalanar type or a normal stagger type thin film transistor, wherein the thin film transistor is formed on a glass substrate, and the semiconductor thin film according to any one of claims 1, 2, 3, 4, 5, 6, 7, 8 and 9 is used in an active layer of the thin film transistor, and a film thickness of a gate insulation film of the thin film transistor is thinner than 80 nm or a ratio of the film thickness of the gate insulation film to a film thickness of the active layer is smaller than 8/6.
 21. A semiconductor apparatus containing a copalanar type or a normal stagger type thin film transistor, wherein the thin film transistor is formed on a glass substrate, and the semiconductor thin film according to any one of claims 1, 2, 3, 4, 5, 6, 7, 8 and 9 is used in an active layer of the thin film transistor, and a film thickness of a gate insulation film of the thin film transistor is thinner than a film thickness of the active layer.
 22. A semiconductor apparatus containing a thin film transistor according to any one of claims 16, 17, 18, 19, 20 and 21, wherein the glass substrate is made of a no-alkali glass which has a softening point lower than 700° C.
 23. A semiconductor apparatus containing a solar cell, wherein a semiconductor thin film formed at least in a first layer in semiconductor layers of the solar cell through a laser crystallizing method has a thickness thicker than 40 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm.
 24. A semiconductor apparatus containing a solar cell, wherein a semiconductor thin film formed at least in a first layer in semiconductor layers of the solar cell through a laser crystallizing method has a thickness thicker than 40 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when a surface area of an arbitrary crystal grain is expressed by Sn and a circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2).
 25. A semiconductor apparatus containing a solar cell, wherein a semiconductor thin film formed at least in a first layer in semiconductor layers of the solar cell through a laser crystallizing method has a thickness thicker than 40 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when a surface area of an arbitrary crystal grain is expressed by Sn and a circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2), and further when crystal structures on an arbitrary cross section of the crystalline semiconductor thin film are observed, at least more than 70% of the crystal grains continuously extend from an interface between the semiconductor layer and a base layer to the semiconductor surface without discontinuity at some midpoint.
 26. A semiconductor apparatus containing a solar cell, wherein the semiconductor thin film according to any one of claims 1, 2, 3, 6, 7, 8 and 9 is used at least in a first layer in semiconductor layers of the solar cell.
 27. A method of fabricating a semiconductor apparatus containing a thin film transistor, wherein the method of fabricating the semiconductor thin film according to any one of claims 10, 11, 12, 13, 14 and 15 is applied to fabrication of an active layer of the thin film transistor.
 28. A method of fabricating a semiconductor apparatus containing a solar cell, wherein the method of fabricating the semiconductor thin film according to any one of claims 10, 11, 12, 13, 14 and 15 is applied to fabrication of at least a first layer in semiconductor layers of the solar cell.
 29. A semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel or a peripheral circuit, wherein a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the thin film transistor according to claims 16, 17, 18, 19, 20, 21 and 22 is used for the drive element in the pixel or the peripheral circuit of the active matrix type liquid crystal display apparatus.
 30. A method of fabricating a semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel or a peripheral circuit, wherein a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the method of fabricating a thin film transistor according to claim 27 is applied to fabrication of the thin film transistor of the active matrix type liquid crystal display apparatus.
 31. A semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel and one of electrodes of a signal storage capacitor in the pixel is formed of a semiconductor thin film in the same layer as an active layer of the thin film transistor, wherein a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the semiconductor thin film forming the one of electrodes of a signal storage capacitor in the pixel of the active matrix type liquid crystal display apparatus has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm.
 32. A semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel and one of electrodes of a signal storage capacitor in the pixel is formed of a semiconductor thin film in the same layer as an active layer of the thin film transistor, wherein a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the semiconductor thin film forming the one of electrodes of the signal storage capacitor in the pixel of the active matrix type liquid crystal display apparatus has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when a surface area of an arbitrary crystal grain is expressed by Sn and a circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2).
 33. A semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel and one of electrodes of a signal storage capacitor in the pixel is formed of a semiconductor thin film in the same layer as an active layer of the thin film transistor, wherein a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the semiconductor thin film forming the one of electrodes of the signal storage capacitor in the pixel of the active matrix type liquid crystal display apparatus has a film thickness within a range of 40 nm to 100 nm; an average roughness of the surface smaller than 5 nm; and an average size of the crystal grains larger than 500 nm, wherein when a surface area of an arbitrary crystal grain is expressed by Sn and a circumferential length on the surface of the arbitrary crystal grain is expressed by Ln, at least more than 50% of the crystal grains satisfy the relation Ln≦4πRn where Rn=(Sn/π)^(1/2), and further when crystal structures on an arbitrary cross section of the crystalline semiconductor thin film are observed, at least more than 70% of the crystal grains continuously extend from an interface between the semiconductor layer and a base layer to the semiconductor surface without discontinuity at some midpoint.
 34. A semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel and one of electrodes of a signal storage capacitor in the pixel is formed of a semiconductor thin film in the same layer as an active layer of the thin film transistor, wherein a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the semiconductor thin film forming the one of electrodes of the signal storage capacitor in the pixel is the semiconductor thin film according to any one of claims 4, 5, 6, 7, 8 and
 9. 35. A method of fabricating a semiconductor apparatus containing an active matrix type liquid crystal display apparatus in which a thin film transistor is used as a drive element in a pixel and one of electrodes of a signal storage capacitor in the pixel is formed of a semiconductor thin film in the same layer as an active layer of the thin film transistor, wherein a no-alkali glass having a softening point lower than 700° C. is used for a supporting substrate, and the method of fabricating the semiconductor thin film according to any one of claims 10, 11, 12, 13, 14 and 15 is applied to fabrication of the semiconductor thin film forming the one of electrodes of the signal storage capacitor in the pixel.
 36. A method of fabricating a semiconductor thin film or a semiconductor apparatus according to any one of claims 10, 11, 12, 13, 14, 15, 27, 28, 29, 30 and 35, wherein the semiconductor thin film or the semiconductor apparatus is fabricated using an apparatus in which at least a film forming apparatus for forming a semiconductor thin film and a laser crystallizing apparatus are connected to each other by a transfer apparatus having an evacuating apparatus.
 37. A method of fabricating a semiconductor thin film or a semiconductor apparatus according to any one of claims 10, 11, 12, 13, 14, 15, 27, 28, 29, 30 and 35, wherein the semiconductor thin film or the semiconductor apparatus is fabricated using an apparatus in which at least a film forming apparatus for forming a semiconductor thin film, a film forming apparatus for forming an insulation film and a laser crystallizing apparatus are connected to each other by transfer apparatuses each having an evacuating apparatus.
 38. A method of fabricating a semiconductor thin film or a semiconductor apparatus according to any one of claims 36 and 37, wherein the atmosphere of the transfer apparatus is maintained in a vacuum below 10⁻⁵ torr or an atmosphere of an inert gas such as nitrogen, helium, neon, argon or the like.
 39. A method of fabricating a semiconductor thin film or a semiconductor apparatus according to any one of claims 10, 11, 12, 13, 14, 15, 27, 28, 29, 30 and 35, wherein the semiconductor thin film or the semiconductor apparatus is fabricated using an in-line type apparatus in which at least a film forming portion for forming a semiconductor thin film, a laser crystallizing portion and a transfer portion are placed in a single chamber. 